I-PVB Resin ye-PVB interlayer nezinye izinhlelo zokusebenza
Isithombe somkhiqizo
| Izinja | Khuphuka | Ukuhlolwa kwe-Yellowness | Shula into Okuqukethwe (%) | Hydroxyl Okuqukethwe (%) | Iqembu le-Acetal Okuqukethwe (%) | Udizima | Ukudluliselwa Kokukhanya | Melt Index @ 120 ℃ (g / 10min) | Mahhala Okuqukethwe (%) | I-Viscosity (10.0% PVB Solution) MPA.S | Ubuningi obuningi (g / 100ml) |
| I-PVB interlayer | I-DVB201 | Awekho ama-yeellowness abonakalayo | ≦ 1.5 | 17.0 ~ 20.0 | 75-80 | ≤0.40 | ≥87.0 | 0.90 -1.70 | ≤0.0100 | I-1000 ~ 1400 | ≥ 14.0 |
| DVB202 | Awekho ama-yeellowness abonakalayo | ≦ 1.5 | 17.0 ~ 20.0 | 75-80 | ≤0.40 | ≥87.0 | 1.30 -2.10 | ≤0.0100 | 900 ~ 1300 | ≥ 14.0 | |
| I-elekthronikhi ye-ceramic, ukunamathela, inki | Khuphuka | Shula into Okuqukethwe (%) | -Obudlova Aldehyde Okuqukethwe (WT%) | Hydroxyl Okuqukethwe (WT%) | Mahhala Okuqukethwe (%) | Ukuhlakanipha 23 ℃ (MPA.S) | |||||
| I-DVB402 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦ 0.50 | 10 ~ 30 | ||||||
| DVB412 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦ 0.50 | 30 ~ 50 | ||||||
| DVB413 | ≦ 3.0 | 71.0 ~ 74.0 | 24.0 ~ 27.0 | ≦ 0.50 | I-10 ~ 60 | ||||||
| DVB422 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦ 0.50 | 50 ~ 80 | ||||||
| DVB432 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦ 0.50 | I-100 ~ 170 | ||||||
| DVB433 | ≦ 3.0 | 71.0 ~ 74.0 | 24.0 ~ 27.0 | ≦ 0.50 | I-140 ~ 220 | ||||||
| DVB462 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦ 0.50 | 40 ~ 90 * | ||||||
| DVB463 | ≦ 3.0 | 71.0 ~ 74.0 | 24.0 ~ 27.0 | ≦ 0.50 | 60 ~ 120 * | ||||||
* ngo-5%Isixazululo se-Ethanol, abanye bangu-10%Isixazululo se-Ethanol